Organic Semiconductors (OSC)

p-Type Organic Semiconductors

Organic field-effect transistors (OFETs) have been good attentions as mechanically flexible and lightweight materials. Printed flexible devices for active layer made from organic semiconductor materials can be manufactured by means of low-cost and environment-friendly coating processes, and are particularly expected as next-generation electronics.

A newly line-up of highly soluble p-type semiconductor materials with high hole mobility is available from FUJIFILM Wako. These products are new materials developed by the joint research with Prof. Dr. Takeya and Assoc. Prof. Dr. Okamoto of The University of Tokyo and FUJIFILM Corporation.

Features

01238_img01.png
  • High hole mobility
    The hall mobility is over 5 cm2/Vs.
  • High heat resistance
    The products do not deteriorate even when used at the temperature required for OSC patterning.
  • High solubility
    Solubility in toluene : 0.5 wt%
  • High repeatability
    Good repeatability was confirmed in the characterization of the transistor by Pi-Crystal, Inc.
  • Sublimated products
    The purity of over 99% is guaranteed

Summary of various transistor element characteristics

  • Film production method Substrate temperature(℃) µmax
    (cm2/Vs)a
    Vth (V)b Ion/ Ioff
    Drop-casting 40 4.0 -21 - -37 106
    Edge-casting 40 6.2 -15 - -20 106
    Vacuum deposition 60 1.8 -15 - -20 106
    100 1.0 -15 - -20 106

    a)Evaluated in the saturation region. b) The gate insulator is SiO2 with a thickness of 200 nm.

  • 01238_img02.png

Crystal film fabrication by edge casting method and transistor characterization evaluation

TBBT-C4

  • 01238_img03.png

    01238_img04.png
  • Coating film formation conditions
    Solvent Toluene
    Concentration 0.05 wt%
    Melted temperature 60 ℃
    Hot plate temperature 50 ℃
    Substrate SiO2 200 nm
    SAM β-PTS
    Drop amount 1 drop
    Drying Under pressure, 50℃, 8h

 

01238_img05.png


TBBT-C10

  • 01238_img06.png

    01238_img07.png
  • Coating film formation conditions
    Solvent Anisole
    Concentration 0.05 wt%
    Melted temperature 70 ℃
    Hot plate temperature 40 ℃
    Substrate SiO2 200 nm
    SAM β-PTS
    Drop amount 1 drop
    Drying Under pressure, 70℃, 24h

 

01238_img11.png

References

  1. Okamoto, T. and Takeya, J. et al.: Adv. Mater., 25, 6392 (2013).
  2. Okamoto, T. et al.: J. Mater. Chem. C, 5, 1903 (2017).

Product List

  • Open All
  • Close All

p-Type Organic Semiconductors

n-Type Organic Semiconductors

Organic Semiconductor Building Block

Related Product List

  • Open All
  • Close All

For research use or further manufacturing use only. Not for use in diagnostic procedures.

Product content may differ from the actual image due to minor specification changes etc.

If the revision of product standards and packaging standards has been made, there is a case where the actual product specifications and images are different.

+49-2131-311-271

Reception hours: Mon-Fri 9:00 - 15:00 (CET)For other hours than the above, please contact us via the inquiry form.